Physicochemical and mechanical techniques were carried out to characterize three concrete tyre-rubber waste dosages such as 5, 10 and 15%, w/w. The elastomeric material was identified as styrene-butadiene rubber (SBR). It was observed that the growing SBR content in the mixture decreased the concrete performance. The best results were presented by 5% w/w tyre-rubber waste concrete sample. This composition was tested at Mourão hydroelectric powerplant spillway as repairing material.

Last decade Brazilian rivers experimented progressive biofouling of Limnoperna fortunei communities and Cordylophora caspia hydroids. The microhabitat is so favorable that in around 1.5 years L. fortunei increased from 0.39 to nearby 149,000 units/m². Ten Portland cement mortar samples were produced with 1: 3.5: 0.4 dosages and installed for 1 year at Salto Caxias Brazilian Power Plant reservoir in 0.5 m and 1.0 m deep to investigate the biofouling influence on hydraulic civil structures. SEM, EDS, visual investigation and XRF results indicate none direct chemical interrelationships between L. fortunei and the mortar samples. However C. caspia diminished the mortar surface resistance and caused cement paste leaching.

The influence of natural aging furthered by atmospheric corrosion of parts of electric transformers and materials, as well as of concrete poles and cross arms containing corrosion inhibitors was evaluated in Manaus. Results for painted materials, it could showed that loss of specular gloss was more intensive in aliphatic polyurethane points than in acrylic polyurethane ones. No corrosion was observed for metal and concrete samples until 400 days of natural aging. Corrosion in steel reinforcement was noticed in some poles, arising from manufacturing faults, such as low cement content, water/cement ratio, thin concrete cover thickness, etc. The performance of corrosion inhibitors was assessed by many techniques after natural and accelerated aging in a 3.5% saline aqueous solution. The results show the need for better chemical component selection and its concentration in the concrete mixture.

An alternative application of the humid sludge from the Passaúna WTP, located in Curitiba's metropolitan area, is proposed for concrete structures, partially replacing aggregates and cement. For the investigation, a reference concrete and four concrete mixtures with sludge were produced, and from these, two mixtures, containing 4% and 8% of sludge (m/m), were analyzed by different techniques: X ray fluorescence, X ray diffraction, thermo-gravimetric analysis, physicochemical analysis, compressive strength, etc. The properties were evaluated and the results indicate that the mixtures can be applied in different situations as cast structures for construction of concrete walls. Mixtures with more than 4% of sludge are restricted to applications where the workability of the concrete is not required, such as for residential pavements, sidewalks and stepping floors.